We manufacture a wide range of fluxes, which can be put to varied uses. Fluxes consist of mild organic acid or strong inorganic acid which promotes high speed cleaning of metals with strong surface oxides and are generally used for silver brazing, copper brazing, solder and aluminum.
Product Code
Applications
Remarks
SILFLUX
It is an all Purpose, low temperature flux for use in brazing both
ferrous and
non-ferrous
metals and alloys using silver brazing filler
metals. It begins to
melt and dissolve oxides
at 340°C and becomes
fully molten at about
600°C and provides adequate protection
upto
750°C. Excellent in hot
rodding
operation used to braze weld
where the hot
brazing rod is
plunged into the
dry powder.
It can be easily cleaned up in hot water.
Equivalent to
Esab Rupatam
A Flux
SILFLUX-A
Recommended for use in 650°C-815°C Excellent in hot rodding operations. For
application where a dry volatile flux is required. It can be easily cleaned up.
Equivalent to
Handy Dry Flux
6040
SILFLUX-B
The temperature range of this flux is 600°C-925°C. It is recommended for brazing
tungsten and chromium carbides, molybdenum alloys and high chromium stainless
steels. It is useful where local overheating may occur, as in fast induction heating.
Available in powder and paste form.
Equivalent Handy
Flux Type B-1
SILPASTE
It is general purpose, low temperature flux in paste form which provides creamy
smooth consistency and excellent adhesion. It begins to melt and dissolve oxides at
320°C, is fully molten at 600°C and it provides full protection upto 870°C. It is used for
brazing all ferrous and non-ferrous alloys.It can be easily cleaned up in hot water.
Equivalent to
Handy Paste Flux.
BRAZOFLUX
It is used for brazing or fusion welding of various ferrous and non-ferrous metals and
alloys ( like cast iron, steel, brass et.) using Cu-Zn (Brass) filler metals.
Equivalent to
Esab Brazotectic
Flux.
BRONZOFLUX
It is used for brazing various ferrous and non-ferrous metals and alloys using Cu-Sn
(Bronze) based filler metals.